Aim To evaluate the resistance of the union between a glass fiber post and radicular dentine after cleaning the root with 17% EDTA and filling with different endodontic cements. Methods Forty uniradicular bovine incisors were removed to obtain root lengths of 18 mm. Endodontic treatment was performed on all roots using different filling cements (zinc oxide and eugenol-based, OZE; cement based on epoxy resin, AH) and cleaning solutions (saline, SA or EDTA), which made it possible to obtain four groups: OZESA, OZEEDTA, AHSA and AHEDTA. Subsequently, 12 mm of filling material was removed from the roots, and they were prepared to receive fiber posts luted with resin cement. To execute the mechanical cycles (2x106 cycles, 90 N, 4 Hz), coronal reconstruction was performed with a silicon matrix. The roots were then sliced (2-mm thick) to perform the push-out test. The results were analyzed using analysis of variance (one factor and two factors) and Tukey’s test (α=0,05). Results Bond strength (Mpa) was significantly higher for OZEEDTA (9,18) and AHEDTA (8,70) than for OZESA (6,06) AHSA (8,7). OZEEDTA also presented the highest values in the cervical region (15,18) but was significantly lower in the apical region (2,99). However, AHEDTA had a homogeneous bond strength in all thirds. Conclusion Regardless of the endodontic cement used, EDTA was used as an irrigating solution, culminating in a higher bond strength between the glass fiber post and dentin.

ABSTRACT Objective: To identify the lingual foramina in a Brazilian population of 210 individuals through Cone-Beam Computed Tomography images, in order to guide the installation of dental implants in the region of the mental symphysis. Methods: After identifying the lingual foramina on a parasagittal section, four measurements were taken: distance to the alveolar ridge, distance to the mandibular lower border, distance to the limit of the vestibular cortical, and alveolar ridge inclination angle. The measurements were compared in relation to gender by the Mann-Whitney test. The association between gender and the number of foramina was done by the chi-square test. Pearson’s correlation analyzed the linear relationship between age and number of foramina. Results: Lingual foramina are present in 99.6% of the research participants. In the upper-inferior direction, a mean distance to the alveolar ridge of 21.4 mm was noted, while the mean distance to the lower mandibular border was 13.1 mm. In the bucco-lingual direction, a mean distance from the lingual foramina to the vestibular cortical of 15.2 mm is noted. The inclination angle of the alveolar ridge had a mean of 25.4º. Regarding gender, the test was not significant only for the distance to the vestibular cortical. Conclusion: The lingual foramina had a descending way in 100% of cases, being positioned mainly in the middle thirds (66.5%) and lower thirds (32.7%) of the mandibular ridge height. The use of dental implants up to 13 mm in length and up to 4 mm in diameter in the region of the symphysis mentualis is recommended.

RESUMO Objetivos: Identificar as foraminas linguais em uma população brasileira de 210 indivíduos, por meio de imagens de tomografia computadorizada de feixe cônico, a fim de orientar a instalação de implantes dentários em região de sínfise mentual. Métodos: Após identificação das foraminas linguais em corte parasagital, foram realizadas quatro medidas: distância até à crista alveolar, distância até à borda inferior da mandíbula, distância até o limite da cortical vestibular e ângulo de inclinação do rebordo alveolar. As medidas foram comparadas em relação ao sexo pelo teste Mann-Whitney. A comparação entre os sexos e o número de foraminas foi feito pelo teste qui-quadrado. A correlação de Pearson analisou a relação linear entre idade e número de foraminas. Resultados: As foraminas linguais estão presentes em 99,6% dos indivíduos. No sentido súpero-inferior, nota-se uma distância média até à crista alveolar de 21,4 mm, enquanto a distância média até à borda inferior da mandíbula foi de 13,1 mm. No sentido vestíbulo-lingual, nota-se uma distância média da foramina lingual até a cortical vestibular de 15,2 mm. O ângulo de inclinação do rebordo alveolar apresentou uma média de 25,4º. Em relação ao sexo, o teste só não foi significativo para a distância até a cortical vestibular. Conclusão: As foraminas linguais apresentam um trajeto descendente em 100% dos casos, posicionando-se, principalmente, nos terços médios (66,5%) e terços inferiores (32,7%) da altura do rebordo mandibular. Recomenda-se o uso de implantes dentários de até 13 mm de comprimento e de até 4mm de diâmetro em região de sínfise mentual.

ABSTRACT: This study aimed to compare the effect of four irrigation solutions for post space cleaning on the bond strength between glass fiber post and root dentine. Forty bovine roots were root-filled and randomly divided into four groups (n=10), according to the irrigation solution: CG (Control Group): saline solution; SH (Sodium Hypochlorite Group); CLX (Chlorhexidine group) and EDTA (ethylenediaminetetraacetic acid group). Specimens were submitted to mechanical aging and push-out test. Statistical analysis (ANOVA two-way and Tukey test; p<0.05) was performed. A stereomicroscope was used for failure mode classification. EDTA showed higher bond strength values, differing statistically from SH and CG (p<0.05). Adhesive failure between dentin and resinous cement was predominant, followed by mixed failures. SEM images showed pronounced smear layer removal in the EDTA group. 17 % EDTA was better than other solutions for cleaning of post space when using glass fiber posts.

RESUMEN: Este estudio tuvo como objetivo comparar el efecto de cuatro soluciones de irrigación para la limpieza del espacio del poste sobre la fuerza de unión entre el poste de fibra de vidrio y la dentina radicular. Se rellenaron cuarenta raíces bovinas y se dividieron aleatoriamente en cuatro grupos (n = 10), según la solu- ción de riego: CG (Grupo Control): solución salina; SH (Gru- po de hipoclorito de sodio); CLX (grupo clorhexidina) y EDTA (grupo ácido etilendiaminotetraacético). Las muestras se sometieron a una prueba de envejecimiento mecánico y de expulsión. Se realizó análisis estadístico (ANOVA bidireccional y prueba de Tukey; p <0,05). Se utilizó un microscopio estereoscópico para la clasificación del modo de falla. EDTA mostró valores de fuerza de unión más altos, difiriendo estadísticamente de SH y CG (p <0,05). Pre-dominó la falla adhesiva entre dentina y cemento resinoso, seguida de fallas mixtas. Las imágenes SEM mostraron una eliminación pronunciada de la capa de frotis en el grupo de EDTA. El EDTA al 17 % fue mejor que otras soluciones para la limpieza del espacio de los postes cuando se utilizan postes de fibra de vidrio.

RESUMO O objetivo do estudo foi avaliar o histórico de quedas e investigar as condições de saúde e fatores de risco para sua ocorrência em idosos cadastrados nas unidades da Estratégia de Saúde da Família. Foram entrevistados 163 idosos cadastrados em dez unidades da Estratégia de Saúde da Família, por meio da aplicação de questionário estruturado para caracterização da presença de doenças autorreferidas, quedas nos últimos 12 meses, características da moradia e recebimento de visitas de profissionais de saúde. Além disso, os idosos foram submetidos a uma avaliação antropométrica. O índice de quedas foi de 31,3%, sendo que o gênero (p=0,032), o autorrelato de muitos móveis na residência (p=0,013) e a presença de doenças cardiometabólicas/respiratórias (p=0,024) são os fatores que se relacionam significantemente com a ocorrência de quedas no último ano. Os idosos do grupo quedas apresentaram maior índice de massa corporal (p=0,014) e maior número de doenças cardiometabólicas/respiratórias (p=0,015) e neuropsicológicas (p=0,049). Aproximadamente um terço dos idosos caíram no último ano, e a maior presença de quedas ocorreu em mulheres e em idosos que apresentaram maior presença de doenças cardiometabólicas/respiratórias e neuropsicológicas, além de maior índice de massa corporal e muitos móveis na residência.

ABSTRACT This study aimed to evaluate the history of falls and investigate health conditions and risk factors for falls in elderly subjects enrolled in the Family Health Strategy units. One hundred sixty-three elderly subjects registered in ten Family Health Strategy units were interviewed by applying a structured questionnaire to characterize living conditions, self-reported diseases, the occurrence of falls in the last 12 months, housing characteristics, and receiving visits from a health professional. In addition, the elderly underwent an anthropometric assessment. The results indicate a fall rate of 31.3%, with gender (p=0.032), self-report of how much furniture at home (p=0.013), and the presence of cardiometabolic/respiratory diseases (p=0.024) being the factors that are significantly related to the presence of falls in the last year. Elderly fallers had higher body mass index (p=0.014) and higher number of cardiometabolic/respiratory (p=0.015) and neuropsychological diseases (p=0.049). It can be concluded that approximately one-third of the elderly fell in the last year. A greater presence of falls occurs in women and the elderly with a higher presence of cardiometabolic/respiratory and neuropsychological diseases, in addition to higher body mass index and furniture at home.

RESUMO Objetivo Avaliar a influência do tratamento térmico do silano na resistência de união entre dois cimentos resinosos e uma cerâmica feldspática CAD/CAM. Métodos Quarenta blocos cerâmicos foram duplicados em resina micro-híbrida. Todas as cerâmicas foram condicionadas com ácido fluorídrico 10% por 20 s e receberam aplicação do silano. Os blocos foram randomizados em oito grupos (n = 5): P-Panavia F; PAg- Panavia F + Envelhecimento; HP-Tratamento térmico + Panavia F;HPAg-Tratamento térmico + Panavia F + Envelhecimento; R-RelyX ARC; RAg-RelyX ARC; HR-Tratamento térmico + RelyX ARC; HRAg - Tratamento térmico + RelyX ARC + Envelhecimento. O tratamento térmico foi realizado em forno a 100 °C durante2 min. Todos os blocos foram cimentados e cortados para obter amostras para microtração. Foram feitos 10000 ciclos térmicos. As amostras foram submetidas a teste de micro-tração. Resultados O teste ANOVA revelou uma interação significativa entre cimento/tratamento térmico (p=0,001) e tratamento térmico/ciclo térmico (p=0,001). Conclusão Dessa maneira, o tratamentotérmico do silano a 100ºC por 2 minutos foi capaz de aumentar a resistência de união entre o cimento resinoso e uma cerâmica feldspática mesmo após o envelhecimento.

ABSTRACT Objective Evaluate the influence of silane heat treatment in bond durability between two resin cements and CAD/CAM feldspathic ceramic. Methods 40 feldspathic ceramic blocks were obtained, and were duplicated in microhybrid composite. All ceramic blocks were etched with 10% hydrofluoric acid for 20 s and received application of silane agent. The blocks were randomizedinto eight groups (n=5) according to the surface treatments and luting agents: P- Panavia F; PAg- Panavia F + Aging; HP- Heat Treatment + Panavia F; HPAg- Heat Treatment + Panavia F + Aging; R- RelyX ARC; Rag- RelyX ARC + Aging; HR- Heat Treatment + RelyX ARC; HRAg- Heat Treatment + RelyX ARC + Aging. The heat treatment was performed in furnace at 100 °C for 2 min. All blocks were cemented and cut to obtain samples with adhesive area of 1 mm2. Aging was performed with 10000 thermal cycles. The samples were subjected to microtensile bond strength test. Results The three-way ANOVA test revealed a significant interaction between cement versus heat treatment (p=0.001) and heat treatment versus thermal cycling (p=0.001) indicating that there was a change in bond strength due to surface treatment and aging. Conclusion Therefore, the heat treatment of the silane at 100 ºC for 2 minutes obtained higher values of bond strength between the resin cement and a feldspathic ceramicafter aging.

Abstract To evaluate the effect of different surface treatments on the marginal misfit and retentive strength between Y-TZP crowns and an epoxy resin. Forty (40) epoxy resin (G10) abutments (height: 5mm, conicity: 60, finish line: large chamfer) with equal dimensions were milled and included in polyurethane to simulate the periodontal ligament. Next, 40 Y-TZP crowns (thickness: 1mm) were milled (Cerec in Lab) and randomly divided into four groups (n=10) according to the surface treatment: GS(glaze spray), GP(glaze powder/liquid), P(zirconia primer) and RS(tribochemical silica coating). The conditioned surfaces were cemented with dual self-adhesive cement, light cured and submitted to thermomechanical cycling (2x106, 100N, 4Hz, 5°/55°C). Marginal misfit was analyzed by a stereomicroscope and SEM. Retentive strength test was performed (1mm/min) until crown debonding. Glaze layer thickness was also performed to GS and GP groups. Marginal misfit data were analyzed by Kruskal Wallis and Dunn tests; one-way ANOVA and Tukey (5%) analyzed the tensile strength data. The marginal misfit of the GS (48.6±19.9μm) and GP (65.4±42.5μm) were statistically lower than the RS (96±62.9μm) and P (156±113.3μm) (p=0.001). The retentive strength of the GP (470.5±104.1N) and GS (416.8±170.2N) were similar to the P (342.1±109.7N), but statistically higher than those of the RS (208.9±110N). The GS and GP glaze layer was 11.64μm and 9.73μm respectively. Thus, glaze application promoted lower marginal discrepancy and higher retentive strength values than conventional techniques.

Resumo: O objetivo deste estudo foi avaliar o efeito de diferentes protocolos de polimento sobre a rugosidade e morfologia superficial de uma cerâmica à base de dissilicato de lítio (IPS e.max CAD). Foram confeccionadas 50 barras cerâmicas (2,0x3,0x2,5 mm), separadas aleatoriamente em cinco grupos (n=10), conforme os tratamentos de superfície: C: Controle; BC: Borracha Ceramaster (60 s); RP: Roda de pano impregnado granulação grossa (30 s) + Roda de pano impregnado granulação fina (30 s); BE: Borracha Exa-Cerapol cinza (20 s) + Borracha Exa-Cerapol rosa (20 s) + Borracha Cerapol Super (20 s); RF: Roda de feltro com pasta diamantada grossa (30 s) + roda de feltro com pasta diamantada fina (30 s). As amostras foram avaliadas quantitativamente quanto à rugosidade superficial (Ra) e qualitativamente em MEV, em diferentes momentos: inicialmente (antes da asperização), após asperização e após os polimentos. As médias de Ra foram submetidas aos testes estatísticos ANOVA (two-way) e Tukey (p<0,05). Após os diferentes protocolos de polimento, não foi possível observar diferenças significativas entre os grupos BC e BE (p=0,6347), entre BE e RP (p=0,1366) e RP e RF (p=0,5433). Comparando as diferentes etapas de um mesmo grupo foi possível observar que os grupos RP (p<0,0001) e RF (p<0,0001) apresentaram diferenças significativas. Em MEV, os grupos BC e BE apresentam um padrão morfológico superficial semelhante ao grupo controle. Todos os sistemas de polimento foram efetivos na redução da rugosidade de superfície para o mesmo padrão de cerâmica.

Abstract: The aim of this study was to evaluate the effect of different polishing protocols on surface roughness and morphology of lithium disilicate ceramics (IPS e.max CAD). Fifty ceramic bars (2.0x3.0x2.5 mm) were produced and randomly divided into five groups (n=10), according to surface treatments: C: Control; Cer: Ceramaster (60 s); CW: cloth wheel with large-grit diamond (30 s) + cloth wheel with fine-grit diamond paste (30 s); E: grey Exa-Cerapol (20 s) + pink Exa-Cerapol (20 s) + Cerapol Super (20 s); F: Felt wheel with large-grit diamond paste (30 s) + Felt wheel with fine-grit diamond paste (30 s). The samples were evaluated quantitatively for surface roughness (Ra) and qualitatively by SEM, at different moments: initial (prior to roughening), after roughening and after polishing procedures. Ra means were submitted to two-way ANOVA and Tukey test (p<0.05). After the different polishing protocols, no statistically significant differences were observed between the Cer and E groups (p=0.6347), E and CW groups (p=0.1366), and CW and FW groups (p=0.5433). Comparing different stages in the same group, it was possible to observe that CW (p<0.0001) and FW groups (p<0.0001) showed significant differences. SEM analysis revealed that both Cer and E groups exhibited a surface morphological pattern similar to that of control group. All polishing systems were effective in reducing the surface roughness of the studied ceramic type.

Este estudo avaliou o efeito de diferentes formas de tratamento térmico de um silano pré-hidrolisado na adesão de um cimento resinoso à base de monómeros fosfatados (MDP) à uma cerâmica vítrea. Blocos em resina e cerâmica feldspática (n=48, n=6 para teste de união, n=2 para microscopia) foram divididos aleatoriamente em 4 grupos e submetidos a tratamentos de superfície: G1-ácido fluorídrico (HF) 9,6% por 20 s + Silano + cimento resinoso com MDP (Panavia F) ; G2-HF 9,6% por 20 s + Silano + Tratamento Térmico (forno) + Panavia F; G3-Silano + Tratamento Térmico (forno) + Panavia F; G4-HF 9,6% por 20 s + Silano + Tratamento Térmico (ar quente) + Panavia F; G5-Silano + Tratamento Térmico (ar quente) + Panavia F; G6-Silano + Panavia F. Teste de microtração (MTBS) foi realizado utilizando máquina de ensaios universal (1 mm/min). Após o descolamento, substrato e superfícies aderentes foram analisadas utilizando estereoscópico e microscópio eletrônica de varredura (MEV) para classificação dos tipos de falha. Os dados foram analisados estatisticamente utilizando o teste ANOVA dois fatores e o teste de Tukey (=0,05). O tratamento térmico do silano contendo MDP, com condicionamento prévio com HF (G2:13,15±0,89a e G4:12,58±1,03a) resultou em valores de resistência de união significativamente superiores aos do grupo controle (G1:9,16±0,64b). Os grupos sem condicionamento prévio (G3:10,47±0,70b e G5:9,47±0,32b), apresentaram valores de resistência de união estatisticamente semelhantes entre eles e ao controle (G1). O silano utilizado sem condicionamento prévio e tratamento térmico apresentou os menores valores de resistência de união (G6:8,05±0,37c). As análises em MEV mostraram predominância de falhas adesivas e as análises em EDS demonstraram espectros com elementos semelhantes (Si, Na, Al, K, O, C) caracterizando a microsestrutura da vitro-cerâmica estudada. O tratamento térmico do silano pré-hidrolisado contendo MDP, realizado em forno a 100 °C durante 2 min ou com ar quente a 50±5 °C durante 1 min, foi eficaz no aumento dos valores de união entre cimento resinoso contendo MDP e cerâmica.

This study evaluated the influence of different forms of heat treatment on a pre-hydrolyzed silane to improve the adhesion of phosphate monomer-based (MDP) resin cement to glass ceramic. Resin and feldspathic ceramic blocks (n=48, n=6 for bond test, n=2 for microscopy) were randomly divided into 6 groups and subject to surface treatments: G1: Hydrofluoric acid (HF) 9.6% for 20 s + Silane + MDP resin cement (Panavia F); G2: HF 9.6% for 20 s + Silane + Heat Treatment (oven) + Panavia F; G3: Silane + Heat Treatment (oven) + Panavia F; G4: HF 9.6% for 20 s + Silane + Heat Treatment (hot air) + Panavia F; G5: Silane + Heat Treatment (hot air) + Panavia F; G6: Silane + Panavia F. Microtensile bond strength (MTBS) test was performed using a universal testing machine (1 mm/min). After debonding, the substrate and adherent surfaces were analyzed using stereomicroscope and scanning electron microscope (SEM) to categorize the failure types. Data were analyzed statistically using two-way test ANOVA and Tukey's test (=0.05). Heat treatment of the silane containing MDP, with prior etching with HF (G2: 13.15±0.89a; G4: 12.58±1.03a) presented significantly higher bond strength values than the control group (G1: 9.16±0.64b). The groups without prior etching (G3: 10.47±0.70b; G5: 9.47±0.32b) showed statistically similar bond strength values between them and the control group (G1). The silane application without prior etching and heat treatment resulted in the lowest mean bond strength (G6: 8.05±0.37c). SEM analysis showed predominantly adhesive failures and EDS analysis showed common elements of spectra (Si, Na, Al, K, O, C) characterizing the microstructure of the glass-ceramic studied. Heat treatment of the pre-hydrolyzed silane containing MDP in an oven at 100 °C for 2 min or with hot air application at 50±5 ºC for 1 min, was effective in increasing the bond strength values between the ceramic and resin cement containing MDP.

AIM: To evaluate the influence of plaster condition, dry or not, on the amount of residual monomer in heat-cured acrylic resin. METHODS: Thirty acrylic resin specimens (65x10x3 mm) were fabricated and randomly assigned to 5 groups (n=6). The evaluated resins were heat-cured acrylic resins by conventional or microwave polymerization techniques and the plaster was previously dried in microwave oven in two groups. Each specimen was individually immersed in a test tube containing methanol (7 days) for surface analysis. In the groups for which internal monomer was evaluated, the specimens were fragmented and the small fragments were weighed prior to immersion in methanol. The analysis was made by high performance liquid chromatography (HPLC). Data were analyzed by ANOVA and Tukey test (p<5%) RESULTS: showed statistical differences among the groups. CONCLUSIONS: The previous plaster drying influenced the residual monomer amount showing a decrease of these levels.

The aim of this study was to evaluate the effects of external bleaching agents on morphology of human enamel after excessive homemade dental bleaching. 20 intact human third molars were submitted to mesio-distal crosscut and embedded in polystyrene resin. The specimens were submitted to finish and a half of enamel surface of each specimen was covered with cosmetic varnish, meaning control group (G0). The specimens were randomly divided into four groups (n=10): G1 1 bleaching session by 16% carbamide peroxide; G2 3 bleaching sessions by 16% carbamide peroxide; G3 1 bleaching session by 22% carbamide peroxide; G4 3 bleaching sessions by 22% carbamide peroxide. Each session lasted 8 hours a day, during two weeks, with 45 days of interval between sessions. In this period, the specimens were kept in artificial saliva at 37°C. The specimens were observed by scanning electron microscopy and the results showed depression areas, irregularities, erosion, and enamel prisms exposition, which was more evident in G4. It can be concluded that the excess of bleaching produced many alterations on enamel surface, mainly when was used carbamide peroxide in higher concentration.

El objetivo de este estudio fue evaluar los efectos en la morfología externa del esmalte humano al utilizar excesivamente agentes blanqueadores dentales de uso casero. Se cortaron 20 intactos terceros molares humanos en sentido mesiodistal, luego fueron sumergidas las porciones radiculares en resina de poliestireno. Las muestras fueron pulidas, cubriendo la mitad de la superficie del esmalte con barniz cosmético, representando así al grupo control (G0). Las muestras fueron distribuidas aleatoriamente en cuatro grupos (n=10): G1-Una sesión de blanqueamiento con peróxido de carbamida al 16%, G2. Tres sesiones de blanqueamiento con peróxido de carbamida al 16%, G3-Una sesión de blanqueamiento con peróxido de carbamida al 22%, G4- Tres sesiones de blanqueamiento con peróxido de carbamida al 22%. Cada sesión tuvo una duración de 8 horas diarias durante dos semanas con 45 días de intervalo entre sesiones. Durante ese periodo las muestras fueron mantenidas en saliva artificial a 37°C. Las muestras fueron observadas al microscopio electrónico de barrido, mostrando aéreas de depresión, irregularidades, erosiones y exposición de prismas del esmalte. Esto fue más evidente en G4. Se puede concluir que el exceso de blanqueamiento producido muchas alteraciones en la superficie del esmalte, sobre todo cuando se utilizó peróxido de carbamida en alta concentración.